Analysis of the Impact and Bending Strength of Coconut Coir Fiber-Reinforced Polyester Resin Composite Material for Automotive Bumper Applications
Keywords:
coconut coir fiber, polyester composite, impact strength, flexural strength, automotive bumper.
Abstract
The automotive industry requires lightweight, durable, cost-effective, and environmentally friendly materials to improve vehicle performance and sustainability. This study investigates the effect of coconut coir fiber volume fraction and fiber orientation on the impact and flexural strength of polyester matrix composites intended for automotive bumper applications. Composite specimens were fabricated using the hand lay-up method with three fiber orientations: random, unidirectional, and laminated. Impact and flexural tests were conducted according to ASTM standards, and the experimental data were analyzed using Two-Way ANOVA. The results revealed that fiber volume fraction significantly affected impact strength (p = 0.043 < 0.05), indicating that higher fiber content improved the composite's ability to absorb impact energy. In contrast, fiber orientation and the interaction between fiber volume fraction and fiber orientation showed no significant effect on impact strength. Furthermore, neither fiber volume fraction, fiber orientation, nor their interaction significantly influenced flexural strength (p > 0.05). These findings demonstrate that fiber volume fraction is the dominant factor affecting the impact performance of coconut coir fiber-reinforced polyester composites. Therefore, the developed composite shows promising potential as a sustainable alternative material for automotive bumper applications.
References
Abidin, N. M. Z., Sultan, M. T. H., Shah, A. U. M., & Safri, S. N. A. (2019). Charpy and Izod impact properties of natural fibre composites. IOP Conference Series: Materials Science and Engineering, 670(1), 012031.
Adi, A., et al. (2024). Analisis pengaruh komposisi terhadap nilai uji impak pada material komposit hybrid serat pinang dan serat kelapa. Jurnal Teknologi Rekayasa Teknik Mesin.
Adiananda, A., & Batan, I. M. L. (2015). Pengembangan bumper depan mobil pick up multiguna pedesaan. Jurnal Teknik ITS, 4(1), 6–9. ISSN: 2337-3539
Ahmad, A. A. (2018). Sejarah perkembangan bumper kenderaan. The Patriots. https://thepatriots.asia/sejarah-perkembangan-bumper-kenderaan/
Ahyani, A. S. (2018). Pemeriksaan kekuatan bending dan impak untuk blok rem kereta api dengan karbon ekuivalen 4,86%. Universitas Gadjah Mada.
Akbar, N. F. (2018). Pembuatan dan karakterisasi tekan dan impak komposit hybrid serat ijuk acak/serat gelas anyam bermatrik polyester. Jurnal Tugas Akhir Teknik Mesin Universitas Muhammadiyah Yogyakarta, 1–8.
Alrosyid, M. (2023). Analisis desain bumper mobil terhadap keselamatan kendaraan. Jurnal Teknologi Otomotif, 9(1), 45–52.
API. (2022). Laporan tahunan Asosiasi Produsen Otomotif Indonesia. APOI.
Asrofi, I.M., Putra, W.T., dan Winardi, Y., (2023). Pengaruh Campuran Plastik Waste LDPE dan PET Bermatrik Resin Polyester terhadap Kekuatan Tarik dan Struktur Mikro. Jurnal Sains, Teknologi dan Informatika.10(1). 51-58.
Ariska, L. P. A., Sahlan, M. A., & Hikmah, U. (2023). Analisis sifat mekanis komposit matriks polyester dengan penguat cangkang kerang hijau. Jurnal Fisika, 13(1), 20–28. DOI: https://doi.org/10.15294/jf.v13i1.38835
ASTM International. (2021). ASTM D790: Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials. ASTM International.
ASTM International. (2019). ASTM E23: Standard test methods for notched bar impact testing of metallic materials. ASTM International.
ASTM International. (2021). ASTM D7264/D7264M-21: Standard test method for flexural properties of polymer matrix composite materials. ASTM International.
ASTM International. (2018). ASTM D256: Standard test methods for determining the Izod pendulum impact resistance of plastics. ASTM International.
ASTM International. (2017). ASTM D790: Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials. ASTM International.
Atiqoh, N., Wulandari, D., Ryandadari, D., & Ganda, A. N. F. (2023). Pengaruh variasi arah serat bambu terhadap kekuatan impak komposit sebagai material bumper mobil. Jurnal Rekayasa Mesin, 8(2), 114–119. DOI: https://doi.org/10.26740/jrm.v8i02.54783
Belingardi, G., & Obradovic, J. (2010). Design of automotive bumper systems for pedestrian protection. International Journal of Crashworthiness, 15(3), 277–287.
Bifel, R. D. N., Maliwemu, E. U. K., & Adoe, D. G. H. (2015). Pengaruh perlakuan alkali serat sabut kelapa terhadap kekuatan tarik komposit polyester. Lontar, 2(1), 61–68.
Callister, W. D., & Rethwisch, D. G. (2018). Materials science and engineering: An introduction (10th ed.). New Jersey: John Wiley & Sons.
Daniel, I. M., & Ishai, O. (2006). Engineering mechanics of composite materials (2nd ed.). Oxford University Press.
Davis, J. R. (2004). Tensile testing (2nd ed.). ASM International.
Dermawan, W. R., Pambudi, R. F., Hifani, R., Sembada, I. V., & Musaffa, Q. S. (2018). Pengaruh variasi fraksi volume komposit serat sabut kelapa unsaturated polyester terhadap pengujian tarik. Jurnal Rotor, 11(1), 22–24. DOI: https://doi.org/10.33504/jitt.v1i2.62
Dermawan, W. R., Pambudi, R. F., Hifani, R., Sembada, I. V., & Musaffa, Q. S. (2022). Pengaruh variasi fraksi volume serat sabut kelapa komposit unsaturated polyester terhadap kekuatan bending. Stator, 2(1), 31–32.
Destya, Y. (2012). Proses pembuatan body kit (bumper) mobil dari komposit serat tebu dengan matriks resin polyester. (Skripsi, Universitas Islam Indonesia). URI: https://dspace.uii.ac.id/handle/123456789/36333
Farrel, D., Yuliyanto, Y., & Zulfitriyanto, Z. (2022). Pengaruh sifat mekanik komposit serat sabut kelapa bermatrik polyester terhadap pengujian tarik dan kelenturan. Jurnal Indonesia Sosial Teknologi, 3, 219–230.
Faruk, O., Bledzki, A. K., Fink, H. P., & Sain, M. (2012). Natural fiber reinforced composites: A review. Progress in Polymer Science, 37(11), 1552–1596. DOI: https://doi.org/10.1016/j.progpolymsci.2012.04.003
Fiore, V., Scalici, T., Di Bella, G., & Valenza, A. (2015). A review on basalt fibre and its composites. Composites Part B: Engineering, 74, 74–94.
Gautama, R. C., Alfatih, M. F., & Alimi, S. (2022). Eksperimen uji bending pada komposit resin polyester dan epoxy serat jerami padi dengan proses hand lay-up. Teknika STTKD, 8(2), 237–242.
Gere, J. M., & Goodno, B. J. (2013). Mechanics of materials (8th ed.). Cengage Learning.
Gibson, L. J. (2016). Principles of composite material mechanics (4th ed.). Florida: CRC Press.
Gibson, L. J., & Ashby, M. F. (1997). Cellular solids: Structure and properties (2nd ed.). Cambridge: Cambridge University Press.
Grasse Zur. (2023). 3- & 4-point bending test according to ASTM D7264. Retrieved from https://grassezur.de
Gundara, G., & Rahman, M. B. N. (2019). Sifat tarik, bending dan impak komposit serat sabut kelapa–polyester dengan variasi fraksi volume. Jurnal Material dan Proses Manufaktur, 2(1), 1–8.
Gunadarma. (2023). Proses manufaktur front bumper mobil X di PT Sugity Creatives. (Skripsi, Universitas Gunadarma).https://library.gunadarma.ac.id/ repository/ proses-manufaktur-front-bumper-mobil-x-di-pt-sugity-creatives-ssm
Halimi, A. D. (2017). Uji eksperimen tingkat kekerasan dan ketangguhan baja pegas JIS SUP 9. Jurnal Teknik Mesin UNESA, 5(3). 45–52.
Hermawan. (2023). Analisis kekuatan impak komposit berpenguat serat rami dengan matriks gondorukem pada fraksi massa 15% dan 30%. Jurnal Teknik Mesin, 11(1).
Hestiawan, H., Jamasri, J., & Kusmono, K. (2017). Pengaruh penambahan katalis terhadap sifat mekanis resin poliester tak jenuh. Teknosia, 3(1), 1–7.
Hidayat, T., Susanto, A., & Prabowo, D. (2022). Analisis hubungan kekuatan impak dan bending pada komposit serat alam berbasis polyester. Jurnal Teknik Mesin Indonesia, 17(2), 85–92.
Joshi, S. V., Drzal, L. T., Mohanty, A. K., & Arora, S. (2004). Are natural fiber composites environmentally superior to glass fiber reinforced composites? Composites Part A, 35(3), 371–376.
Koronis, G., Silva, A., & Fontul, M. (2013). Green composites for automotive applications. Composites Part B, 44(1), 120–127.
Kurniawan, N. A., Setiawan, F., & Sofyan, E. (2022). Pengujian tarik komposit serat pisang dengan metode hand lay-up. Teknika STTKD, 8(2), 281–288.
Kusmono. (2024). Pengembangan material komposit serat alam untuk aplikasi industri berkelanjutan. Universitas Gadjah Mada.
Li, C., Liu, Z., Xue, K., Huo, Y., Li, F., & Zhu, X. (2023). The Catalytic Curing Reaction and Mechanical Properties of a New Composite Resin Matrix Material for Rocket Fuel Storage Tanks. Applied Sciences, 13(21), 11790. https://doi.org/10.3390/app132111790
Lochan, P. P., & Polak, M. A. (2024). Evaluation of 3-point and 4-point bending tests for tensile strength assessment of GFRP bars. Materials, 17(21), 5261.
Lumintang, R., Rauf, F. A., & Soplanit, G. D. (2019). Ketahanan bending komposit matriks poliester berpenguat serat sabut kelapa. Jurnal Tekno Mesin, 5(2). 88–94.
Mallick, P. K. (2007). Fiber-reinforced composites: Materials, manufacturing, and design (3rd ed.). CRC Press.
Mawardi, I., Husin, N., Zaini, Z., Usman, U., Saifuddin, S. (2022). Karakteristik kekuatan impak dan kekerasan hybrid biokomposit berbasis epoksi yang diperkuat serat sabut kelapa dan serat sintetis. Multitek Indonesia. 16(1). 1–8. 10.24269/mtkind.v16i1.5102.
Mujika, F. (2006). On the difference between flexural moduli obtained by three-point and four-point bending tests. Polymer Testing, 25(2), 214–220.
Ongki, R. I., Zaldi S.S., & Ariyanto (2021). Pengaruh Parameter Proses 3D Printing Terhadap Kekuatan Impak Menggunakan Metode Charpy Pada Filamen PLA. SNITT. Prosiding Seminar Nasional Inovasi Teknologi Terapan.
Perwara, A. S. (2024). Pengaruh persentase katalis terhadap sifat mekanis komposit bermatrik resin polyester. Approach: Jurnal Teknologi Penerbangan, 5(2).
Pickering, K. L., Efendy, M. G. A., & Le, T. M. (2016). Recent developments in natural fibre composites. Composites Part A, 83, 98–112.
Pratama, R., & Nugroho, S. (2020). Pemanfaatan serat sabut kelapa sebagai penguat komposit untuk aplikasi otomotif. Jurnal Rekayasa Material, 9(3), 120–128.
Purnomo, H., & Satridjo, D. (2011). Desain dan analisa impact bumper kendaraan SUV dengan metode elemen hingga. Rotasi, 13(1), 24–32.
Rahmadan, S., Prawatya, Y. E., Lubis, G. S. (2024). Analisis pengaruh variasi fraksi volume terhadap kekuatan impak komposit hybrid. Jurnal Teknologi Rekayasa Teknik Mesin. 6(2), 80–87.
Rahmawati, S. D., & Widodo, S. (2021). Effect of alkali treatment on thermal conductivity of coconut coir fiber reinforced polyester composites. Journal of Natural Fibers, 18(5), 789–798.
Rizaldi, F. A., & Drastiawati, N. S. (2023). Analisa pengaruh perendaman NaOH terhadap kekuatan komposit. Jurnal Teknik Mesin, 11(3), 27–34.
Rochim, M. N., & Ningsih, T. H. (2021). Penggunaan serat jerami padi dalam material bumper mobil. Jurnal Teknik Mesin, 9(3), 1–6.
Rusly, M., Sulistyowati, R., & Toruan, P. L. (2023). Analisis uji tarik komposit serat batang kelakai. Journal of Physics, 9(1), 43–48.
Samaluddin, S., Mubarak, A. A., Djunuda, R., Fauzan, F., & Takdir, R. A. (2024). Analisis kekuatan material komposit berdasarkan variasi resin dan katalis pada material kapal berbahan fiberglass. Jurnal Ilmiah Giga, 27(2), 96–104.
Sapuan, S. M. (2014). Composite materials: Selection, design and applications. CRC Press.
Saputra, R., Kardiman, K., Santoso, D. T., & Imran, A. I. (2022). Analisis sifat mekanis komposit serat sabut kelapa dan bambu. Jurnal Rekayasa Mesin, 17(1), 37–48.
Sari, D. P., Wijaya, H., & Lestari, N. (2021). Pengaruh ukuran spesimen terhadap distribusi tegangan pada uji bending komposit serat alam. Jurnal Teknik Industri, 12(1), 33–40.
Satria, G.M.I.B., Hastuti S., & Taufik I., (2024). Pengaruh Penambahan Serat Pohon Bambu Ampel (Bambusa Vulgaris) pada Komposit Hybrid untuk Material Bumper Kendaraan Bermotor. Jurnal Teknik Mesin, Industri, Elektro dan Informatika. 3(4).148-156.
Setiawan, I. K., Suardana, N. P. G., & Suyasa, I. W. B. (2018). Pengaruh variasi fraksi volume terhadap kekuatan tarik pada komposit polyester berpenguat serat daun praksok. Jurnal Teknik Desain Mekanik, 7(2),
Sugiyono. (2019). Metode penelitian kuantitatif, kualitatif, dan R&D (Edisi revisi). Bandung: Alfabeta.
Sirait, R.I., (2012). Analisis Sifat Mekanis Sandwich Composite Serat Bambu dengan Core Serbuk Kelapa Melalui Uji Three Point Bending dan Uji Tekan. (Skripsi, Fakultas Teknik Mesin dan Dirgantra Institut Teknologi Bandung). URI: https://digilib.itb.ac.id/assets/files/FTMD/AE/2012/2012_ TA_13606025_RIZANUL_IKHWAN_SIRAIT.pdf.
TestResources, Inc. (2026, March 15). A complete guide to the three-point bending flexural test. TestResources.
Titani, F. R., Imalia, C. L., & Haryanto. (2018). Pemanfaatan serat sabut kelapa sebagai material penguat pengganti fiberglass pada komposit resin polyester untuk aplikasi bahan konstruksi pesawat terbang. Jurnal Techno (Jurnal Fakultas Teknik Universitas Muhammadiyah Purwokerto), 19(1), 1–6. https://doi.org/10.30595/techno.v19i1.2397
Tulak, J.Y., Hamsina dan Al-Gozali (2023). Kualitas Briket Dari Limbah Kayu Mahoni Dengan Menggunakan Perekat Kanji Dan Resin Sebagai Pengisi. Jurnal SEINTIS, 4(2), 121-133.
Wibowo, A., Firmansyah, M., & Setiawan, E. (2021). Karakterisasi patahan komposit serat sabut kelapa akibat beban lentur. Jurnal Ilmiah Teknik Mesin, 10(2), 67–74.
Winoto, R. A., Wulandari, D., Utama, F. Y., & Ganda, A. N. F. (2023). Rancang bangun prototype bumper mobil berbasis uji impact. Jurnal Rekayasa Mesin, 8(2), 135–140. https://doi.org/10.26740/jrm.v8i02.54953
Yan, L., Chouw, N., & Jayaraman, K. (2014). Flax fibre and its composites. Composites Part B, 56, 296–317.
Adi, A., et al. (2024). Analisis pengaruh komposisi terhadap nilai uji impak pada material komposit hybrid serat pinang dan serat kelapa. Jurnal Teknologi Rekayasa Teknik Mesin.
Adiananda, A., & Batan, I. M. L. (2015). Pengembangan bumper depan mobil pick up multiguna pedesaan. Jurnal Teknik ITS, 4(1), 6–9. ISSN: 2337-3539
Ahmad, A. A. (2018). Sejarah perkembangan bumper kenderaan. The Patriots. https://thepatriots.asia/sejarah-perkembangan-bumper-kenderaan/
Ahyani, A. S. (2018). Pemeriksaan kekuatan bending dan impak untuk blok rem kereta api dengan karbon ekuivalen 4,86%. Universitas Gadjah Mada.
Akbar, N. F. (2018). Pembuatan dan karakterisasi tekan dan impak komposit hybrid serat ijuk acak/serat gelas anyam bermatrik polyester. Jurnal Tugas Akhir Teknik Mesin Universitas Muhammadiyah Yogyakarta, 1–8.
Alrosyid, M. (2023). Analisis desain bumper mobil terhadap keselamatan kendaraan. Jurnal Teknologi Otomotif, 9(1), 45–52.
API. (2022). Laporan tahunan Asosiasi Produsen Otomotif Indonesia. APOI.
Asrofi, I.M., Putra, W.T., dan Winardi, Y., (2023). Pengaruh Campuran Plastik Waste LDPE dan PET Bermatrik Resin Polyester terhadap Kekuatan Tarik dan Struktur Mikro. Jurnal Sains, Teknologi dan Informatika.10(1). 51-58.
Ariska, L. P. A., Sahlan, M. A., & Hikmah, U. (2023). Analisis sifat mekanis komposit matriks polyester dengan penguat cangkang kerang hijau. Jurnal Fisika, 13(1), 20–28. DOI: https://doi.org/10.15294/jf.v13i1.38835
ASTM International. (2021). ASTM D790: Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials. ASTM International.
ASTM International. (2019). ASTM E23: Standard test methods for notched bar impact testing of metallic materials. ASTM International.
ASTM International. (2021). ASTM D7264/D7264M-21: Standard test method for flexural properties of polymer matrix composite materials. ASTM International.
ASTM International. (2018). ASTM D256: Standard test methods for determining the Izod pendulum impact resistance of plastics. ASTM International.
ASTM International. (2017). ASTM D790: Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials. ASTM International.
Atiqoh, N., Wulandari, D., Ryandadari, D., & Ganda, A. N. F. (2023). Pengaruh variasi arah serat bambu terhadap kekuatan impak komposit sebagai material bumper mobil. Jurnal Rekayasa Mesin, 8(2), 114–119. DOI: https://doi.org/10.26740/jrm.v8i02.54783
Belingardi, G., & Obradovic, J. (2010). Design of automotive bumper systems for pedestrian protection. International Journal of Crashworthiness, 15(3), 277–287.
Bifel, R. D. N., Maliwemu, E. U. K., & Adoe, D. G. H. (2015). Pengaruh perlakuan alkali serat sabut kelapa terhadap kekuatan tarik komposit polyester. Lontar, 2(1), 61–68.
Callister, W. D., & Rethwisch, D. G. (2018). Materials science and engineering: An introduction (10th ed.). New Jersey: John Wiley & Sons.
Daniel, I. M., & Ishai, O. (2006). Engineering mechanics of composite materials (2nd ed.). Oxford University Press.
Davis, J. R. (2004). Tensile testing (2nd ed.). ASM International.
Dermawan, W. R., Pambudi, R. F., Hifani, R., Sembada, I. V., & Musaffa, Q. S. (2018). Pengaruh variasi fraksi volume komposit serat sabut kelapa unsaturated polyester terhadap pengujian tarik. Jurnal Rotor, 11(1), 22–24. DOI: https://doi.org/10.33504/jitt.v1i2.62
Dermawan, W. R., Pambudi, R. F., Hifani, R., Sembada, I. V., & Musaffa, Q. S. (2022). Pengaruh variasi fraksi volume serat sabut kelapa komposit unsaturated polyester terhadap kekuatan bending. Stator, 2(1), 31–32.
Destya, Y. (2012). Proses pembuatan body kit (bumper) mobil dari komposit serat tebu dengan matriks resin polyester. (Skripsi, Universitas Islam Indonesia). URI: https://dspace.uii.ac.id/handle/123456789/36333
Farrel, D., Yuliyanto, Y., & Zulfitriyanto, Z. (2022). Pengaruh sifat mekanik komposit serat sabut kelapa bermatrik polyester terhadap pengujian tarik dan kelenturan. Jurnal Indonesia Sosial Teknologi, 3, 219–230.
Faruk, O., Bledzki, A. K., Fink, H. P., & Sain, M. (2012). Natural fiber reinforced composites: A review. Progress in Polymer Science, 37(11), 1552–1596. DOI: https://doi.org/10.1016/j.progpolymsci.2012.04.003
Fiore, V., Scalici, T., Di Bella, G., & Valenza, A. (2015). A review on basalt fibre and its composites. Composites Part B: Engineering, 74, 74–94.
Gautama, R. C., Alfatih, M. F., & Alimi, S. (2022). Eksperimen uji bending pada komposit resin polyester dan epoxy serat jerami padi dengan proses hand lay-up. Teknika STTKD, 8(2), 237–242.
Gere, J. M., & Goodno, B. J. (2013). Mechanics of materials (8th ed.). Cengage Learning.
Gibson, L. J. (2016). Principles of composite material mechanics (4th ed.). Florida: CRC Press.
Gibson, L. J., & Ashby, M. F. (1997). Cellular solids: Structure and properties (2nd ed.). Cambridge: Cambridge University Press.
Grasse Zur. (2023). 3- & 4-point bending test according to ASTM D7264. Retrieved from https://grassezur.de
Gundara, G., & Rahman, M. B. N. (2019). Sifat tarik, bending dan impak komposit serat sabut kelapa–polyester dengan variasi fraksi volume. Jurnal Material dan Proses Manufaktur, 2(1), 1–8.
Gunadarma. (2023). Proses manufaktur front bumper mobil X di PT Sugity Creatives. (Skripsi, Universitas Gunadarma).https://library.gunadarma.ac.id/ repository/ proses-manufaktur-front-bumper-mobil-x-di-pt-sugity-creatives-ssm
Halimi, A. D. (2017). Uji eksperimen tingkat kekerasan dan ketangguhan baja pegas JIS SUP 9. Jurnal Teknik Mesin UNESA, 5(3). 45–52.
Hermawan. (2023). Analisis kekuatan impak komposit berpenguat serat rami dengan matriks gondorukem pada fraksi massa 15% dan 30%. Jurnal Teknik Mesin, 11(1).
Hestiawan, H., Jamasri, J., & Kusmono, K. (2017). Pengaruh penambahan katalis terhadap sifat mekanis resin poliester tak jenuh. Teknosia, 3(1), 1–7.
Hidayat, T., Susanto, A., & Prabowo, D. (2022). Analisis hubungan kekuatan impak dan bending pada komposit serat alam berbasis polyester. Jurnal Teknik Mesin Indonesia, 17(2), 85–92.
Joshi, S. V., Drzal, L. T., Mohanty, A. K., & Arora, S. (2004). Are natural fiber composites environmentally superior to glass fiber reinforced composites? Composites Part A, 35(3), 371–376.
Koronis, G., Silva, A., & Fontul, M. (2013). Green composites for automotive applications. Composites Part B, 44(1), 120–127.
Kurniawan, N. A., Setiawan, F., & Sofyan, E. (2022). Pengujian tarik komposit serat pisang dengan metode hand lay-up. Teknika STTKD, 8(2), 281–288.
Kusmono. (2024). Pengembangan material komposit serat alam untuk aplikasi industri berkelanjutan. Universitas Gadjah Mada.
Li, C., Liu, Z., Xue, K., Huo, Y., Li, F., & Zhu, X. (2023). The Catalytic Curing Reaction and Mechanical Properties of a New Composite Resin Matrix Material for Rocket Fuel Storage Tanks. Applied Sciences, 13(21), 11790. https://doi.org/10.3390/app132111790
Lochan, P. P., & Polak, M. A. (2024). Evaluation of 3-point and 4-point bending tests for tensile strength assessment of GFRP bars. Materials, 17(21), 5261.
Lumintang, R., Rauf, F. A., & Soplanit, G. D. (2019). Ketahanan bending komposit matriks poliester berpenguat serat sabut kelapa. Jurnal Tekno Mesin, 5(2). 88–94.
Mallick, P. K. (2007). Fiber-reinforced composites: Materials, manufacturing, and design (3rd ed.). CRC Press.
Mawardi, I., Husin, N., Zaini, Z., Usman, U., Saifuddin, S. (2022). Karakteristik kekuatan impak dan kekerasan hybrid biokomposit berbasis epoksi yang diperkuat serat sabut kelapa dan serat sintetis. Multitek Indonesia. 16(1). 1–8. 10.24269/mtkind.v16i1.5102.
Mujika, F. (2006). On the difference between flexural moduli obtained by three-point and four-point bending tests. Polymer Testing, 25(2), 214–220.
Ongki, R. I., Zaldi S.S., & Ariyanto (2021). Pengaruh Parameter Proses 3D Printing Terhadap Kekuatan Impak Menggunakan Metode Charpy Pada Filamen PLA. SNITT. Prosiding Seminar Nasional Inovasi Teknologi Terapan.
Perwara, A. S. (2024). Pengaruh persentase katalis terhadap sifat mekanis komposit bermatrik resin polyester. Approach: Jurnal Teknologi Penerbangan, 5(2).
Pickering, K. L., Efendy, M. G. A., & Le, T. M. (2016). Recent developments in natural fibre composites. Composites Part A, 83, 98–112.
Pratama, R., & Nugroho, S. (2020). Pemanfaatan serat sabut kelapa sebagai penguat komposit untuk aplikasi otomotif. Jurnal Rekayasa Material, 9(3), 120–128.
Purnomo, H., & Satridjo, D. (2011). Desain dan analisa impact bumper kendaraan SUV dengan metode elemen hingga. Rotasi, 13(1), 24–32.
Rahmadan, S., Prawatya, Y. E., Lubis, G. S. (2024). Analisis pengaruh variasi fraksi volume terhadap kekuatan impak komposit hybrid. Jurnal Teknologi Rekayasa Teknik Mesin. 6(2), 80–87.
Rahmawati, S. D., & Widodo, S. (2021). Effect of alkali treatment on thermal conductivity of coconut coir fiber reinforced polyester composites. Journal of Natural Fibers, 18(5), 789–798.
Rizaldi, F. A., & Drastiawati, N. S. (2023). Analisa pengaruh perendaman NaOH terhadap kekuatan komposit. Jurnal Teknik Mesin, 11(3), 27–34.
Rochim, M. N., & Ningsih, T. H. (2021). Penggunaan serat jerami padi dalam material bumper mobil. Jurnal Teknik Mesin, 9(3), 1–6.
Rusly, M., Sulistyowati, R., & Toruan, P. L. (2023). Analisis uji tarik komposit serat batang kelakai. Journal of Physics, 9(1), 43–48.
Samaluddin, S., Mubarak, A. A., Djunuda, R., Fauzan, F., & Takdir, R. A. (2024). Analisis kekuatan material komposit berdasarkan variasi resin dan katalis pada material kapal berbahan fiberglass. Jurnal Ilmiah Giga, 27(2), 96–104.
Sapuan, S. M. (2014). Composite materials: Selection, design and applications. CRC Press.
Saputra, R., Kardiman, K., Santoso, D. T., & Imran, A. I. (2022). Analisis sifat mekanis komposit serat sabut kelapa dan bambu. Jurnal Rekayasa Mesin, 17(1), 37–48.
Sari, D. P., Wijaya, H., & Lestari, N. (2021). Pengaruh ukuran spesimen terhadap distribusi tegangan pada uji bending komposit serat alam. Jurnal Teknik Industri, 12(1), 33–40.
Satria, G.M.I.B., Hastuti S., & Taufik I., (2024). Pengaruh Penambahan Serat Pohon Bambu Ampel (Bambusa Vulgaris) pada Komposit Hybrid untuk Material Bumper Kendaraan Bermotor. Jurnal Teknik Mesin, Industri, Elektro dan Informatika. 3(4).148-156.
Setiawan, I. K., Suardana, N. P. G., & Suyasa, I. W. B. (2018). Pengaruh variasi fraksi volume terhadap kekuatan tarik pada komposit polyester berpenguat serat daun praksok. Jurnal Teknik Desain Mekanik, 7(2),
Sugiyono. (2019). Metode penelitian kuantitatif, kualitatif, dan R&D (Edisi revisi). Bandung: Alfabeta.
Sirait, R.I., (2012). Analisis Sifat Mekanis Sandwich Composite Serat Bambu dengan Core Serbuk Kelapa Melalui Uji Three Point Bending dan Uji Tekan. (Skripsi, Fakultas Teknik Mesin dan Dirgantra Institut Teknologi Bandung). URI: https://digilib.itb.ac.id/assets/files/FTMD/AE/2012/2012_ TA_13606025_RIZANUL_IKHWAN_SIRAIT.pdf.
TestResources, Inc. (2026, March 15). A complete guide to the three-point bending flexural test. TestResources.
Titani, F. R., Imalia, C. L., & Haryanto. (2018). Pemanfaatan serat sabut kelapa sebagai material penguat pengganti fiberglass pada komposit resin polyester untuk aplikasi bahan konstruksi pesawat terbang. Jurnal Techno (Jurnal Fakultas Teknik Universitas Muhammadiyah Purwokerto), 19(1), 1–6. https://doi.org/10.30595/techno.v19i1.2397
Tulak, J.Y., Hamsina dan Al-Gozali (2023). Kualitas Briket Dari Limbah Kayu Mahoni Dengan Menggunakan Perekat Kanji Dan Resin Sebagai Pengisi. Jurnal SEINTIS, 4(2), 121-133.
Wibowo, A., Firmansyah, M., & Setiawan, E. (2021). Karakterisasi patahan komposit serat sabut kelapa akibat beban lentur. Jurnal Ilmiah Teknik Mesin, 10(2), 67–74.
Winoto, R. A., Wulandari, D., Utama, F. Y., & Ganda, A. N. F. (2023). Rancang bangun prototype bumper mobil berbasis uji impact. Jurnal Rekayasa Mesin, 8(2), 135–140. https://doi.org/10.26740/jrm.v8i02.54953
Yan, L., Chouw, N., & Jayaraman, K. (2014). Flax fibre and its composites. Composites Part B, 56, 296–317.
Published
2026-06-01
How to Cite
Lalu Moch Syarif Hidayatullah, & Anggit Murdani. (2026). Analysis of the Impact and Bending Strength of Coconut Coir Fiber-Reinforced Polyester Resin Composite Material for Automotive Bumper Applications. International Journal of Technology and Education Research, 4(02), 1062-1082. https://doi.org/10.63922/ijeter.v4i02.3983
.png)
Contact Person +6282139474255
Email : ijeterjournal@gmail.com